Exploring the Specifications and Properties of A413/A413M-07(2012) Steel Grade

Exploring the Specifications and Properties of A413/A413M-07(2012) Steel Grade

A413/A413M-07(2012) refers to the standard specification for carbon steel forgings for general industrial use. This specification covers the chemical composition, mechanical properties, and other requirements for carbon steel forgings.

The chemical composition of A413/A413M-07(2012) steel grade is as follows:

– Carbon (C): 0.25% maximum
– Manganese (Mn): 1.20% maximum
– Phosphorus (P): 0.035% maximum
– Sulfur (S): 0.040% maximum

The mechanical properties of A413/A413M-07(2012) steel grade include:

– Tensile strength: 70,000-95,000 psi (485-655 MPa)
– Yield strength: 36,000-60,000 psi (248-414 MPa)
– Elongation: 16% minimum
– Reduction of area: 30% minimum
– Hardness: 163-217 HB (Brinell hardness)

This steel grade is suitable for the production of various types of forgings used in general industrial applications. It has a good combination of strength, ductility, and toughness, making it suitable for a range of engineering applications. It is commonly used in components such as gears, crankshafts, connecting rods, and valve bodies.

A413/A413M-07(2012) steel grade is commonly used in industries such as automotive, aerospace, and manufacturing. It is widely available and can be heat-treated to enhance its properties, such as hardness and strength.

Overall, A413/A413M-07(2012) steel grade is a versatile and widely used carbon steel forging material that meets the necessary specifications and properties for general industrial applications.